Selective dry oxidation of the ordered Pt–11.1at.% V alloy surface evidenced by in situ temperature-controlled X-ray diffraction

Abstract : A temperature-controlled X-ray diffraction study of the cold-rolled Pt–11.1 at.% V alloy was undertaken to gain better insight into the incomplete transformation of the metastable cubic disordered phase into the tetragonal ordered Pt8V phase, earlier reported by Nxumalo and Lang [11]. This study has revealed a complex behaviour of the alloy when is annealed in primary vacuum. Upon heating above 450 °C, an ordering of vanadium atoms in the Pt–11.1 at.% V alloy leads to the appearance of a tetragonal Pt8V phase. Concomitantly, vanadium atoms at the surface of the ordered alloy are slowly oxidized into V2O3 Corundum type phase by the low oxygen partial pressure existing in primary vacuum. This segregation of vanadium oxide onto the surface depleting the subsurface region in vanadium, an almost pure Pt cubic phase grows at the V2O3-ordered Pt8V alloy interface with increasing the temperature. This investigation also shows that an external selective oxidation of the cold-rolled Pt–11.1 at.% V alloy takes place when is annealed in flowing argon atmosphere.
Type de document :
Article dans une revue
Liste complète des métadonnées

https://hal-univ-lemans.archives-ouvertes.fr/hal-02138601
Contributeur : Gwenaël Corbel <>
Soumis le : jeudi 23 mai 2019 - 21:57:53
Dernière modification le : samedi 3 août 2019 - 01:14:07

Identifiants

Collections

Citation

Gwenaël Corbel, Miroslava Topić, Alain Gibaud, Candace Lang. Selective dry oxidation of the ordered Pt–11.1at.% V alloy surface evidenced by in situ temperature-controlled X-ray diffraction. Journal of Alloys and Compounds, Elsevier, 2011, 509 (23), pp.6532-6538. ⟨10.1016/j.jallcom.2011.03.079⟩. ⟨hal-02138601⟩

Partager

Métriques

Consultations de la notice

27