Effect of fatigue testing on the properties of Glass-Epoxy composites using the acoustic tool

Abstract : This study presents the experimental results of the influence of mechanical fatigue on composite material. The plates of Glass fiber with SR 1500 epoxy resin with SD 2505 composite were realized by vacuum molding. Experimental tests were carried out on a standard hydraulic machine INSTRON 8516. The machine is interfaced with a dedicated computer for controlling and data acquisition. The fatigue tests were performed using sinusoidal type of waveform at a displacement control with frequency of 10 Hz. The evolution of Young’s modulus and strain based on fatigue gives us an idea about the resistance of the material. Degradation of mechanical properties was observed, and the results have showed that the Young’s modulus of plates undergo only minor changes. In fact, the residual stiffness and residual strength decrease when the cycle number of fatigue increase (100 to 50000 cycles), indicating that the studied composites have experienced some forms of mechanical damage.The mechanical tests were backed by Acoustic Emission Monitoring (AEM) during the load cycle, in order to understand the nature of the failure process in the composites such as fiber breakage, matrix crazing, matrix debonding and delamination etc.
Type de document :
Communication dans un congrès
Liste complète des métadonnées

https://hal.archives-ouvertes.fr/hal-02955232
Contributeur : Abderrahim El Mahi <>
Soumis le : jeudi 1 octobre 2020 - 16:15:16
Dernière modification le : lundi 8 février 2021 - 14:27:30

Lien texte intégral

Identifiants

Collections

Citation

Younès Menail, Abderrahim El Mahi, Bachir Redjel, Rachid Berbaoui, Mustapha Assarar. Effect of fatigue testing on the properties of Glass-Epoxy composites using the acoustic tool. 8th International Conference on Manufacturing Science and Education, Jun 2017, Sibiu, Romania. pp.03015, ⟨10.1051/matecconf/201712103015⟩. ⟨hal-02955232⟩

Partager

Métriques

Consultations de la notice

24